Improved Corrosion Resistance of Selective Laser Melted Ti–5Cu Alloy Using Atomized Ti–5Cu Powder

The different types of metal powder used for selective laser melting(SLM) process would cause distinct corrosion behavior due to the uniformity of the obtained microstructure.The SLM-produced Ti–5Cu alloy using atomized Ti–5Cu metal powder(SLMed Ti–5Cu) in this work reveals a relatively uniform microstructure with overwhelming acicular α/α′ phase and shows great advantages on corrosion resistance compared with the SLM-produced Ti–5Cu alloy using the mixture powder(SLMedM Ti–5Cu).The effect of the micro-galvanic cells decreases due to the undetectable Ti_2Cu phase in the microstructure of the SLMed Ti–5Cu.An apparent passivation behavior was observed for SLMed Ti–5Cu instead of severe pitting phenomenon for the SLMed-M Ti–5Cu.The charge transfer resistance of SLMed Ti–5Cu in this work is 10.09 ± 2.63 MΩ cm~2, which is significantly higher than that of SLMed-M Ti–5Cu(4.76 MΩ cm~2).The above result indicates the atomized Ti–5Cu powder plays an important role in the formation of the uniform microstructure of SLMed product, thereby enhancing its corrosion resistance in Hank's solution at 37 ℃.     

Toughness enhancement and equivalent initial fracture toughness of cementitious composite reinforced with aligned steel fibres

Based on theoretical analysis and numerical simulation, the impact of steel fibres on the stress intensity factor (SIF) at the crack tip for cementitious composite was studied. The enhanced toughness of steel fibre reinforced cementitious composite (SFRC) in resisting cracks was explained by the decrement of SIF caused by steel fibre inclusions at the crack tip of the composite. The equivalent initial fracture toughness was used to characterize the crack initiation of SFRC. A simplified method for determining the of SFRC was proposed based on a linear regression method. Fracture tests were conducted on three‐point bending notched beams with different steel fibre volume fractions and specimen sizes to study the crack initiation behaviour of aligned steel fibre reinforced cementitious composite (ASFRC). of ASFRC was calculated, and the size effect of was analysed. The results showed that slightly increased with the steel fibre volume fraction and gradually became stable. For the tested specimens, whose heights varied between 40 and 100 mm, the specimen size had little impact on the .     

多分量数据全波形反演在气藏检测中的关键问题——以苏里格气田为例

苏里格气田是中国典型的致密砂岩气藏，构造简单、平缓，横向非均质性强，有效储层与围岩声学特征差别小，地震响应不明显，常规地震监测方法预测难度大，但气田含气砂岩泊松比低，是地震气藏检测的有效参数。利用弹性全波形反演精度高和能处理复杂非均质介质的优势，反演地层拉梅常数、剪切模量和密度，并计算泊松比，从而进行气藏预测。重点阐述了苏里格气田多分量数据全波形反演初始模型建模、先验模型建模和地震数据预处理3个关键问题的处理方法。二维三分量数据反演和"甜点"预测结果表明：①对于具有强非均质性的苏里格气田，利用全波形反演获得精度较高的地层弹性参数能显著提高气藏预测的准确度；②苏里格地区构造简单、平缓，利用常规叠加速度并结合构造解释可以建立比较好的初始模型，从而有效地解决了周波跳跃和局部极小的难题；③先验知识的约束和地震数据的预处理是全波形反演成功应用于苏里格气田气藏检测的关键。     

轧制与退火对T9S钛合金板材组织与性能的影响

研究了轧制变形量及退火温度对T9S钛合金板材显微组织和室温力学性能的影响。结果表明:增加成品轧制变形量,板材组织破碎更充分,退火后形成等轴α相、拉长α相和晶间β相组织形貌,变形流线比较明显,板材室温强度和硬度升高,伸长率降低,弹性模量增加。随着退火温度升高,板材室温强度和硬度逐渐降低,伸长率逐渐提高,横向弹性模量逐渐减小,纵向弹性模量先增加后减小。经(750~790) ℃×45 min空冷退火处理后的板材可以获得较好的强度和塑性的匹配。     

退火工艺对激光选区熔化成形Ti6Al4V合金组织及室温力学性能的影响

以Ti6Al4V球形粉末为原料,利用激光选区熔化成形方法制备了Ti6Al4V合金试样,采用光学显微镜、扫描电镜及力学性能测试等手段,研究了退火工艺对Ti6Al4V合金室温力学性能及组织的影响规律。结果表明: SLM成形沉积态Ti6Al4V合金室温抗拉强度超过1200 MPa,而平均断后伸长率仅为4.0%;在650 ℃下进行真空退火处理,合金的抗拉强度仍保持在1200 MPa左右,规定塑性延伸强度R_p0.2高于1150 MPa,但试样的断后伸长率<10%;而在750及800 ℃下进行真空退火处理,合金试样的抗拉强度降至1100 MPa左右,规定塑性延伸强度高于1050 MPa,伸长率达到甚至超过10%,材料的综合强韧性得到明显提升。随着真空退火加热温度和保温时间的增加,SLM成形Ti6Al4V合金原始β晶界逐渐变模糊,晶粒趋向于等轴化。与此同时,快速冷却转变的α′针状马氏体未出现明显地粗化。     

Stabilizing temperature-capacitance dependence of (Sr,Pb, Bi)TiO3-Bi4Ti3O12 solutions for energy storage

(1-x)Sr_0.7Pb_0.15Bi_0.1TiO₃-xBi₄Ti₃O₁₂ ((1-x)SPBT-xBIT, x = 0-0.125) bulk ceramics were developed and calcined via the solid-state method, aimed at the application of pulsed power capacitors. The phase structures, temperature stability, hysteresis loop, and discharge properties were systematically investigated. Considering both the temperature stability and dielectric properties, 0.925SPBT-0.075BIT bulk ceramics with a capacitance variation satisfying the X7R specification were developed for pulsed power capacitors. The energy storage density was 0.252 J/cm³, and the ceramics showed high temperature stability at 80 kV/cm. The discharge current waveforms of the 0.925SPBT-0.075BIT ceramics were recorded. A high discharge power density of approximately 1.01 × 10⁸ W/kg with an 8 Ω load resistor and short discharge period of 84 ns were achieved at 50 kV/cm. The good temperature stability properties and high power density show that the 0.925SPBT-0.075BIT ceramics are well suited for pulsed power capacitors with a wide temperature range.     

Structures and properties of chicken myofibrillar protein gel induced by microwave heating

Structures and properties of myofibrillar protein gel prepared at different power (300–800 W) were evaluated. Amino acid analysis demonstrated that changes in microwave power did not alter primary structure of gel. However, an increase in microwave power could change higher structures of gel. As microwave power increased, α-helix content decreased and β-sheet content increased. Increased microwave power probably facilitated protein to unfold and expose the internal groups, causing surface hydrophobicity and the formation of disulphide bonds were enhanced, which indicated changes in tertiary and quaternary structures of protein. At 500 W, gel had the best ultrastructure where surface morphology, springiness and water holding capacity reached the optimum. Our findings suggested that microwave at an appropriate power (500 W) could change higher structures of myofibrillar protein gel to achieve desired processing and quality protein gel characteristics.     

7075铝合金热变形连接接头的组织与性能

应用Gleeble-3500热模拟机对7075铝合金进行了热变形连接试验,利用金相显微镜和扫描电镜对不同温度和保温时间的接头界面组织进行了观察和分析,并对接头进行了拉伸性能测试。结果表明:当连接温度为460 ℃,保温时间为24 h时,对界面进行EDS分析,界面处已经没有氧化物的偏聚,此时的力学性能最佳,抗拉强度达到444 MPa,屈服强度为265 MPa。     

铸态Mg-xSn-1Mn合金的显微组织和阻尼性能

采用光学显微镜(OM)、维氏硬度计、热动态分析仪、X射线衍射(XRD)、多功能内耗仪等,研究了Sn含量对Mg-xSn-1Mn合金显微组织、阻尼性能和力学性能的影响。结果表明:当Sn含量从2%增加到8%时,Mg-xSn-1Mn合金的枝晶间隙呈现细化的趋势,硬度从43.84 HV0.1增加至54.00 HV0.1,呈单调增加的趋势。应变无关阻尼随着Sn含量的增加呈现先增后减的趋势,在Sn含量为4%时达到最大,应变相关阻尼则随着Sn含量的增加呈现逐渐减小的趋势。在低温阶段,相同Sn含量的合金的阻尼随着频率的增大呈现增加的趋势;但在高温下,阻尼值在低频时的上升速率比高频时快,并随着温度的升高,低频阻尼和高频阻尼趋向于相等。当Sn含量不同时,随着温度的升高,Sn含量较高的合金的阻尼值上升速率变快。